摘要/Abstract

摘要：

聚苯醚基材的对称、低活性分子结构使其具有十分稳定的化学性质,因此难以直接利用化学镀技术在基材表面沉积出高质量的金属层。针对此问题,文中采用化学蚀刻与多巴胺接枝相结合的方法对PPO基材进行表面改性处理,以调整表面粗糙度,改善表面亲水性。文中引入对Ag⁺具有吸附作用的活性官能团,提高了沉积金属层的导电性和附着力。各项表征测试证明了经过该方法制备出的铜层呈现出连续、均匀且致密堆积的形貌,并具有高纯度、良好的结晶度、优异的附着力以及低电阻率。

关键词: 聚苯醚, 表面改性, 粗糙度, 多巴胺, 金属层, 化学镀, 导电性, 附着力

Abstract:

The symmetrical and low activity molecular structure of PPO substrate makes it has very stable chemical properties. Therefore, it is difficult to deposit high quality metal layer on the substrate surface by electroless plating. In order to solve this problem, chemical etched and dopamine grafting are combined to treat the surface of the PPO substrate to adjust the surface roughness and improve the surface hydrophilicity. Meanwhile, the conductivity and adhesion of the deposited metal layer are improved by introducing active functional groups that have an adsorption effect on Ag⁺. Characterization tests prove that the copper layer prepared by this method shows a continuous, uniform and densely packed morphology, and has high purity, good crystallinity, excellent adhesion and low resistivity.

Key words: polyphenylene ether, surface modification, roughness, dopamine, metal layer, chemical plating, conductivity, adhesion

中图分类号:

TN04

王康,冯哲圣. 多巴胺改性聚苯醚基材的金属化[J]. 电子科技, 2021, 34(7): 56-60.

WANG Kang,FENG Zhesheng. Metallization of Dopamine Modified Polyphenylene Ether Substrate[J]. Electronic Science and Technology, 2021, 34(7): 56-60.

图/表 8

图1

图2

图3

图4

图5

图6

图7

图8

参考文献 18

[1]	Pawar S P, Biswas S, Kar G P, et al. High frequency millimetre wave absorbers derived from polymeric nanocomposites[J]. Polymer, 2016,84(2):398-419. doi: 10.1016/j.polymer.2016.01.010
[2]	Meng F B, Wang H G, Huang F, et al. Graphene-based microwave absorbing composites: a review and prospective[J]. Composites Part B: Engineering, 2018,137(1):260-277. doi: 10.1016/j.compositesb.2017.11.023
[3]	Yin Y C, Zeng M, Liu J, et al. Enhanced high-frequency absorption of anisotropic Fe₃O₄/graphene nanocomposites[J]. Scientific Reports, 2016(6):1-10.
[4]	高亚丽, 陈苑明, 王守绪, 等. 高速传输中印制电路基板电学性能的研究[J]. 印制电路信息, 2018,26(5):19-23.
	Gao Yali, Chen Fanming, Wang Shouxu. Electical properties of laminates for printed circuit during high-speed transmission[J]. Printed Circuit Information, 2018,26(5):19-23.
[5]	潘志龙. 钛酸钡改性及其聚酰亚胺复合材料的性能研究[J]. 电子科技, 2015,28(3):154-157.
	Pan Zhilong. Surface modification of BaTiO₃ and dielectric properties of modified BaTiO₃/polyimide composites[J]. Electronic Science and Technology, 2015,28(3):154-157.
[6]	龚永林. 新一代印制电路板命脉-高性能基材[J]. 印制电路信息, 2018(8):1-5.
	Gong Yonglin. The lifeblood of new generation PCB—high performance base material[J]. Printed Circuit Information, 2018(8):1-5.
[7]	徐杰. 高频低介损覆铜箔板及其电气绝缘基板的研制[D]. 上海:东华大学, 2016.
	Xu Jie. Study on low dielectric loss coppor-clad plate and its electrical insulating substrate in high frequency[D]. Shanghai:Donghua University, 2016.
[8]	莫晶朝. 高频覆铜板用聚苯醚改性环氧树脂复合材料的制备和性能[D]. 杭州:浙江大学, 2013.
	Mo Jingzhao. Preparation and properties of PPO modified epoxy resin composite materials applied in high requency copper clad laminates[D]. Hangzhou:Zhejiang University, 2013.
[9]	Niknejad S M S, Savoji H, Pourafshari C M, et al. Separation of H₂S from CH₄ by polymeric membranes at different H₂S concentrations[J]. International Journal of Environmental Science and Technology, 2017,14(2):375-384. doi: 10.1007/s13762-016-1156-3
[10]	Zhang Z H, Wu L, Xu T W. Synjournal and properties of side-chain-type sulfonated poly(phenylene oxide) for proton exchange membranes[J]. Journal of Membrane Science, 2011,373(12):160-166. doi: 10.1016/j.memsci.2011.03.002
[11]	Yoshimune M, Haraya K. Flexible carbon hollow fiber membranes derived from sulfonated poly(phenylene oxide)[J]. Separation and Purification Technology, 2010,75(2):193-197. doi: 10.1016/j.seppur.2010.07.017
[12]	Kaewvilai A, Tanathakorn R, Laobuthee A, et al. Electroless copper plating on nano-silver activated glass substrate: A single-step activation[J]. Surface and Coatings Technology, 2017,31(9):260-266.
[13]	Huang J J, Tian C G, Wang J, et al. Fabrication of selective electroless copper plating on PET sheet: Effect of PET surface structure on resolution and adhesion of copper coating[J]. Applied Surface Science, 2018,45(8):734-742.
[14]	Luo L M, Lu Z L, Huang X M, et al. Electroless copper plating on PC engineering plastic with a novel palladium-free surface activation process[J]. Surface and Coating Technology, 2014,25(1):69-73.
[15]	Yi M, Sun H Y, Zhang H C, et al. Flexible fifiber-reinforced composites with improved interfacial adhesion by mussel-inspired polydopamine and poly(methyl methacrylate) coating[J]. Materials Science and Engineering C, 2016,58(3):742-749. doi: 10.1016/j.msec.2015.09.026
[16]	Ding Y H, Floren M, Tan W. Mussel-inspired polydopamine for bio-surface for functionalization[J]. Biosurface and Biotribology, 2016(2):121-136
[17]	Lü Y, Du Y, Chen Z X, et al. Nanocomposite membranes of polydopamine/electropositive nanoparticles/polyethyleneimine for nanofifiltration[J]. Journal of Membrane Science, 2018,54(5):99-106.
[18]	Lee W, Lee J U, Byun J H. Catecholamine polymers as surface modififiers for enhancing interfacial strength of fifiber-reinforced composites[J]. Composites Science and Technology, 2015,11(8):53-61.